The influence of fabricating conditions such as gelization, sintering temperature on crystallinity was studied. The result showed that Bi0.5Na0.5TiO3 was in single phase when compenstation amount of Na in gelization is 40 mol%; sintering temperature higher than 800 oC and sintering time is 2 h. The bandgap of Bi0.5Na0.5TiO3 which estimated from absorption spectroscopy is in the range of 3.01 - 3.18 eV.
Nội dung trích xuất từ tài liệu:
Influence of sintering temperature on phase formation and optical properties of lead free ferroelectric BI0.5NA0.5TIO3 materials