Inhibitive ability and adsorption characteristics of water extract of Thai Nguyen green tea leaver for corrosion of mild steel in 1M HCl solution

Trong bài viết này, các tác giả đã nghiên cứu khả năng ức chế ăn mòn cho thép thường trong dung dịch axit HCl của dịch chiết nước lá chè xanh bằng phương pháp điện hóa. Kết quả nghiên cứu cho thấy ở các nồng độ dịch chiết nước lá chè xanh khác nhau đều có khả năng ức chế ăn mòn thép thường. Hiệu quả ức chế ăn mòn nói chung tăng khi nồng độ dịch chiết tăng.
Nội dung trích xuất từ tài liệu:
Inhibitive ability and adsorption characteristics of water extract of Thai Nguyen green tea leaver for corrosion of mild steel in 1M HCl solutionTạp chí phân tích Hóa, Lý và Sinh học - Tập 19, Số 4/2014INHIBITIVE ABILITY AND ADSORPTION CHARACTERISTICS OF WATEREXTRACT OF THAI NGUYEN GREEN TEA LEAVER FOR CORROSION OF MILD STEEL IN 1M HCL SOLUTION Đến tòa soạn 26 - 5 - 2014 Truong Thi Thao, Pham Thi Hien Luong, Nguyen Dinh Vinh Faculty of Chemistry, Thai Nguyen University of Sciences TÓM TẮTKHẢ NĂNG ỨC CHẾ ĂN MÒN VÀ ĐẶC TRƢNG HẤP PHỤ CỦA DỊCH CHIẾT CHÈ XANH THÁI NGUYÊN ĐỐI VỚI THÉP THƢỜNG TRONG DUNG DỊCH HCL 1MTrong công bố này, chúng tôi đã nghiên cứu khả năng ức chế ăn mòn cho thép thườngtrong dung dịch axit HCl của dịch chiết nước lá chè xanh bằng phương pháp điện hóa.Kết quả nghiên cứu cho thấy ở các nồng độ dịch chiết nước lá chè xanh khác nhau đềucó khả năng ức chế ăn mòn thép thường. Hiệu quả ức chế ăn mòn nói chung tăng khinồng độ dịch chiết tăng. Các nghiên cứu nhiệt động học đã chứng minh rằng sự hấpphụ của dịch chiết chè lên bề mặt thép trong dung dịch axit là tự xảy ra và tuân theothuyết hấp phụ Langmuir. Các kết quả tính toán động học và nhiệt động học chứngminh sự hấp phụ xảy ra theo cơ chế hấp phụ vật lý.Từ khóa: ức chế ăn mòn, thép thường, thuyết hấp phụ đẳng nhiệt Langmuir, hấp phụ vậtlý, chè xanh1. INTRODUCTION carbon chain [1,2]. Green corrosionA corrosion inhibitor, when added in inhibitors are biodegradable and do notminute quantity, decrease the rate of contain heavy metals or other toxiccorrosion of a metal or a metal alloy. compounds. The successful uses ofDue to their industrial importance, most naturally occurring substances to inhibitcorrosion inhibitors have been the corrosion of metals in acidic andsynthesized from cheap raw materials or alkaline environment have been reportedchosen from compounds containing by some research groups [1-8] but thehetero atoms in their aromatic or long application of green tea for this purpose 93has not been investigated much yet. distilled water, dried and immersed inEspecially, green tea also contains study solution.polyphenol promising electrochemical Chemicals and Apparatusperformance as well as the ability to Chemicals used are analytical grade.inhibit corrosion of metal. This research All electrochemical measurements wereconcentrates on the inhibitive and performed in the three-electrode modeadsorptive characteristics of water using a homemade multifunctionalextract of green tea for the corrosion of potentiostat connected to a computermild steel in 1M HCl solution. (Manufactured in Lab of Computer Application to Chemical Research,2. EXPERIMENTAL Institute of Chemistry, Viet Nam Academy of Science and Technology).Extraction of plant A silver/silver chloride electrode and aLeaves of Green tea were collected in piece of stainless steel with large areaThai Nguyen city. The clean air-dried were employed as pseudo-reference andleaves were grounded and extracted 3 counter electrode, respectively. Alltimes with distilled water. After that, experiments were done in unstirred andthree parts of filtered water were further nondeaerated solutions at roomsubjected to evaporation at 353 K. The temperature after immersion for 60 minobtained residue of the extract were in 1M solution with and without additionwashed with n-hexane, dichloromethane, of inhibitor.ethylacetate, n-buthanol, respectively. The linear polarization study was carriedThe final product called water extract out from −20 to +20mV versusW(G) is used to prepare solutions with corrosion potential (Ecorr) at a scan rateits different concentrations by dissolving of 0.1mV.s−1 to determine the0.1, 0.5, 1.0, 2.0, 5.0 and 10.0g in 1 L of polarization resistance (Rp), the1M HCl so ...